15CrNi6/1.5919 Quality Alloy Steel

15CrNi6/1.5919  is a low-alloy steel containing chromium and Nickel as strengthening elements.It has good mechanical property for highly strained parts and good toughness at core tensile strength of 900 – 1200 N/mm². This materail is generally used driving bevel gears, crown wheels, gears, shafts, bolts for automotive and gear components. 15crni6/1.5919

Equivalent Grade Chemical Composition
National
Standard
Grade C% Si% Mn% Cr% Mo% Ni% P% S%
DIN 15CrNi6
(1.5919)
0.14-0.19 ≤0.4 0.4-0.6 1.4-1.7 1.4-1.7 ≤0.025 ≤0.035
Size&Tolerance&Process
Shape Size(mm) Process Tolerance Length(mm)
Round Φ6-Φ50 Cold Drawn H11 3000-5800
Round Φ40-Φ300 Hot Rolled -0/+3mm 3000-10000
Round Φ120-Φ1000 Hot Forged -0/+3mm 3000-10000
Flat/Square/Block Thickness:120-800
Width:120-1500
Hot Forged -0/+3mm 500-6000

Heat Treatment
Normalizing For 15CrNi6
1.Nominal normalizing temperature:850-880°C
2.Hold the temperature for several hours
3.Cooling in the air

Annealing  For 15CrNi6
1.Nominal Annealing temperature:650-700°C
2.Cool slowly in the furance
3.Maximum Brinell hardness of 229

Hardening and Tempering(QT)  For 15CrNi6
1.Nominal Hardening temperature:820-870°C
2.Hold at this temperature then quench in oil or water
3.Tempering  as soon as possible when the temperature low to ambient
4.Heat uniformly to the suitable temperature.
5.keep the material out of the furnace ,then cool in the air

Mechanical Property( for reference only)
1.Tensile strength: 880-1100MPa
2.Yield point: 635MPa
3.Percentage reduction of area after fracture: 40%
4.Elongation after fracture: 11%
5.Impact test (+20°C):  Longitud – 40~60J

Delivery Condition
1.Shape:Round/Square / Flat/Shafts/Rollers/Blocks
2.Surface condition:Black surface/Bright surface
3.Heat Treatment:Normalized/Annealed/QT
4.Straightness:Max 3mm/m(Enhanced straightness may be available on request)
5.Length:3000-5800mm suitable for 20″container.  above 6000mm,suitable for 40″ container
6.Grain Size: 5-8 acc to ASTM E112-96
7.Ultrasonic Standard: Sep1921/ASTM A388/EN 10228-3
8.Non Metallic Inclusion: 2 max acc to ASTM E45 /K4≤20 acc to DIN 50602
9.Forging Ratio: minimum 4 : 1
10.Marking: Grade/Weight/Length/Size/Heat Number

Quality Certification
A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non Metallic Inclusion
5.Heat Treatment Process
6.Grain size
7.Forging ratio
8.NDE test method/criteria

15CrNi6/1.5919 alloy steel manufacturers and suppliers,supplied with round rods,square/flat bars,rollers,shafts,blocks and forging pieces.