1.Chemical Composition For 20MnCr5

	C	Si	Mn	P	S	Cr
Min	0.17		1.1			1.0
Max	0.22	0.4	1.4	0.035	0.035	1.3

2.Related Specifications

• ASTM/AISI:5120
• AFNOR:20MC5
• GB:20CrMn
• JIS:SMnC420

3.Critical Temperature for Heat Treatment of 20MnCr5

• Ac1:765℃
• Ac3:838℃
• Ar1:700℃
• Ar3:798℃
• Austenitizing：940℃

4.Forging 20MnCr5/DIN 1.7147

Forging Temperature:850-1050℃,slow cooling in sands after forged.

20MnCr5 Steel Forging

5.Heat Treatment For 20MnCr5 steel

• Normalizing:880℃-920℃,Cool in air
• Annealing:840-860℃,Cool in furnace,hardness below 187HBW.
• Isothermal Annealing:640-650℃ with harddess 160-170HBW.Structure:Ferrite(F)+Pearlite(P）
• Carburizing: 910-930℃

Surface carbon concentration	Effective hardened layer depth	Surface hardness	Core hardness
0.7-0.85%C	0.7-1.0mm	59-63HRC	33-45HRC

• Case Hardening:810 – 830°C,oil /water quench
• Tempering:180°C – 200°C,air cooling

6.20MnCr5 Steel Mechanical Property with Quenched and Tempered condition

880°C oil quench with 2.5 hours heating, Tempering at 180°C with 1 hour,air cooling

Tensile,Mpa	Yield,Mpa	Elongation,%	Reduction of Area,%	Charpy Impact, J
1130-1570	≥640	≥7	≥45	≥47

7.Supply Size & Condition For 20MnCr5 steel

• Round Bars:  Dia.80 – 1,000mm as Forged
• Flat / Square Bars:  Thickness Max.800mm
• Shafts, Rollers, Blocks:  Customized or According to Drawing
• Rolled Round Bars:  Dia.16 – 300mm with UT Assurance

Heat treatment:Quenched and Tempered (+QT), Normalizing (+N), Annealing (+A)
Surface finish:Black / Rough turned / Peeled

8.Quality Certification
A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non metallic inclusion
5.Heat treatment report
6.Grain size
7.Forging ratio
8.Ultrasonic test report